Microstructural evolution of Al-Cu thin-film conducting lines during post-pattern annealing

1089-7550

AIP Digital Archive

Physics

This work reports a statistical analysis of the evolution of polygranular segment lengths during high-temperature annealing of Al(Cu) thin-film interconnects with quasi-bamboo microstructures. To create samples of Al(Cu) lines that could be imaged by transmission electron microscopy without breaking or thinning, the lines were deposited on electron-transparent silicon nitride films (the "silicon nitride window" technique). The microstructures of the lines were studied as a function of annealing time and temperature. In particular, the distribution of polygranular segment lengths was measured. The results show that the longer polyglranular segments are preferentially eliminated during post-pattern annealing. As a consequence, the segment-length distribution narrows monotonically during annealing, and changes in shape. The preferential loss of the longest polygranular segments leads to a dramatic increase in resistance to electromigration failure.

Electronic Resource