Bolometric detection in a precipitation free Y1Ba2Cu3O7−δ film at 77 K

Chou, Hsiung ; Chen, H. Z. ; Hong, M. T. ; Chen, Y. C. ; Chow, T. C.

Woodbury, NY : American Institute of Physics (AIP)
Published 1996
ISSN:
1077-3118
Source:
AIP Digital Archive
Topics:
Physics
Notes:
A photodetector with high responsivity has been fabricated with a high quality Y1Ba2Cu3O7−δ film on a regular SrTiO3 (100) substrate that has no thinning or etching. The film exhibits a precipitation-free morphology and has an extremely smooth surface having a rms roughness smaller than 5 nm. The film was patterned into a 25×650 μm2 long microbridge by a conventional photolithography technique. The Tco of the microbridge can be tuned by applying different bias currents, which results in a tunable operation temperature of the photodetector at 77.35±1 K. This makes it operationally more practical and economical. The noise voltage at 10 mA bias current is less than the resolution of our setup, 15 nV Hz−0.5. A high responsivity of 2.3×103 V/W was obtained when a bias current of 8 mA and a low power density He–Ne laser of 0.08 J/cm2 s chopped at 2 Hz were applied on the microbridge at 77.35 K. Under the same condition, the noise equivalent power (NEP) and detectivity (D*) have been measured to be 4.34×10−12 W Hz−0.5 and 3×109 cm Hz0.5 W−1, respectively. © 1996 American Institute of Physics.
Type of Medium:
Electronic Resource
URL: