Ermüdungsverhalten von Cu-35%Ni-3,5%Cr nach unterschiedlichen WärmebehandlungenAuszug aus der Dissertation von G.-X. Wang [3]
| ISSN: |
0933-5137
|
|---|---|
| Keywords: |
Chemistry ; Polymer and Materials Science
|
| Source: |
Wiley InterScience Backfile Collection 1832-2000
|
| Topics: |
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
|
| Description / Table of Contents: |
Fatigue Behaviour of Cu-35%Ni-3.5%Cr after Different Heat TreatmentsCu-35%Ni-3.5%Cr has been developed as a substitute for the conventional alloy Cu-30%Ni for marine applications. The Cu-Ni-Cr system exhibits a stable miscibility gap which contains the alloy Cu-35%Ni-3.5%Cr. Therefore, Cu-35%Ni-3.5%Cr can decompose in a wide temperature range. The fatigue behaviour of Cu-35%Ni-3.5%Cr was investigated over a wide decomposition range from solution treated to overaged condition both in air and argon. The most important results will he presented here in a comprehensive form.
|
| Notes: |
Cu-35% Ni-3,5% Cr wurde als Ersatzlegierung für die im Bereich der Meeres- und Schiffbautechnik eingesetzte Legierung Cu-30%Ni entwickelt. Im Cu-Ni-Cr System existiert eine stabile Mischungslücke, in der sich die Legierung Cu-35%Ni-3,5%Cr befindet. Daher ist Cu-35%Ni-3,5%Cr in einem breiten Temperaturbereich entmischbar. Das Ermüdungsverhalten von Cu-35% Ni-3,5%Cr wurde über einen weiten Bereich der Entmischung vom homogenisierten bis hin zum überalterten Zustand sowohl an Luft als auch unter Argon untersucht. Die wichtigsten Befunde werden hier in zusammenfassender Form dargestellt.
|